Hi guys,

I'm a professional glass restorer and am constantly removing hard-water stains from car/boat windows, shower screens etc...

For stage 1 glass corrosion (95% of windows will have at least some of this), I use a product called Winsol Crystal Clear 550 (CC550). This usually removes most of the stains with ease. It works by dissolving the mineral build-up and is the quickest and least messy way of completing the job.

For more stubborn water spots (you can do it this way for light stains too), I use cerium oxide powder which is mixed with demineralised water to form a slurry. I then use a felt pad and polishing tool to polish the stains out. My polishing tool is worth over $1500 but for the DIY guys, you can use a felt pad (purchased from your local hardware store) attached to your household drill and remove the stains this way. It's a lot quicker than polishing by hand but if you have to go down that road, use Superfine Steel Wool (0000 gauge). This is abrasive enough to remove the stains but will not scratch the glass. I get all my supplies from these guys as they are the cheapest around http://fcwc.com.au/shop

Once the glass is restored, I apply a product called Sani-Shield which offers a lasting protection for up to 12 months from the hard-water stains forming again. A cheaper option is RainX

To clean the glass/window/shower screen, simply use soapy solution. You don't want to use anything too harsh otherwise you may compromise the protective sealant.

NEW WEBSITE HERE: http://onlinecleaningsolutions.com.au

  • 4 weeks later...

Something similar, my windows have started to rub on something inside the door and its lightly scratched them. I wanted to get the windows tinted but I'm scared the windows might continue to rub and wear the tint off or that when they lay the tint down the scratches will be seen through the tint. Any tips for maybe removing the scratches or help it from rubbing the glass?

  • 1 month later...

its hard to explain but it basically looks like its peeling and stuff in spots?

i think thats what happened anyway, cos the tint on the familys XC90 was peeling and flaking off in places and when we showed it to tint a car their first reaction was - windex?

ive been told by people who install tinting and final inspection and other good detailers its just unsafe on tint

the people who installed the security tint/film on my house glass also told me not to use windex anymore - microfibre and warm water

the stuff we use to clean windows at my work seems like windex though - and it hasnt caused any damage and ive done more than a 100 cars with it ...

i just wouldnt risk it on any of my cars with so many professionals warning me against it

much cheaper in the long run to just buy a good MF and a good auto glass cleaning solution than to just use windex and find out one day in the future that it buggers up your tint imo

if someone with more knowledge could clear up exactly what it does to tint that would be great cheers.gif

amonia in windex kills tint, turns it purple and peals it off. use glass cleaner designed for tint or just clean water

its hard to explain but it basically looks like its peeling and stuff in spots?

i think thats what happened anyway, cos the tint on the familys XC90 was peeling and flaking off in places and when we showed it to tint a car their first reaction was - windex?

ive been told by people who install tinting and final inspection and other good detailers its just unsafe on tint

the people who installed the security tint/film on my house glass also told me not to use windex anymore - microfibre and warm water

the stuff we use to clean windows at my work seems like windex though - and it hasnt caused any damage and ive done more than a 100 cars with it ...

i just wouldnt risk it on any of my cars with so many professionals warning me against it

much cheaper in the long run to just buy a good MF and a good auto glass cleaning solution than to just use windex and find out one day in the future that it buggers up your tint imo

if someone with more knowledge could clear up exactly what it does to tint that would be great cheers.gif

amonia in windex kills tint, turns it purple and peals it off. use glass cleaner designed for tint or just clean water

  • 3 weeks later...

Hi ,

If your water marks are on the surface of the glass you can remove them using a product by CarPro called Ceriglass. This a Cerium Oxide based product mixed with a nano polish to allow it to work by machine or with the applicator in the kit.

I have removed not only water marks but seriously deep windscreen wiper scratches on glass with this and a polisher. Definitely worth a try.

Click Here for more info.

I have it on my chrome window surrounds and windows. I shall try the acetone trick on the chrome and windows and see how I got.

That Autoglym glass polish is as useless as tits on a bull

  • 4 weeks later...

Where do you get this "ceriglass" you speak of?

JDM Performance,

Your right about that. The product I recommended called Ceriglass does contain cerium oxide as well as nano abrasive acting as a lubricant.

For me, I just clean with soft sponge and liquid soap. Though, hard stains can be clean by ceriglass. There are lot car glasses care material who is very effective in removing car glass stain. Though, it was depend in your usage.

  • 1 month later...
  • 2 weeks later...
  • 2 months later...
  • 2 months later...

Create an account or sign in to comment

You need to be a member in order to leave a comment

Create an account

Sign up for a new account in our community. It's easy!

Register a new account

Sign in

Already have an account? Sign in here.

Sign In Now



  • Similar Content

  • Latest Posts

    • I know this one’s the BB one. My tuner did make mention about the actuator. I am curious about the VCT as well
    • Might also needs a stronger actuator with the right preloading. With older 2019 built bush G3 units, BB upgrade or 21U housing down size makes a pretty decent gain in response as well. 
    • Hey lads  so im finally putting together my rb30 forged bottom end and ran into an issue. I measured my main bearing clearance with arp main studs torqued to 60 ft-lbs using ACL H series STD size bearings and standard, un-ground crank shaft journals and got an oil clearance reading of about 1.3 thou measuring straight up and down and about 2.8 thou measuring at a 45 degree angle (just above and below the parting line). My machine shop said they measured the main tunnel and it was all within spec (they didnt say the actual measurement) and to go with a standard size bearing, which i have done and the clearance is too tight, I'm guessing because of the extra clamping force from the arp studs distorting the main tunnel. I was wanting to run about 2.5 thou main bearing clearance.  My questions are: 1. could i just use the HX extra 1 thou clearance ACL bearings? that would fix my straight up and down clearance making it about 2.3 thou, but then would the side to side clearance be too big at around 3.8 thou? 2. what actually is the recommended main bearing clearance for measuring near the parting line / side to side. i know its supposed to be bigger as the bearing has some eccentricity built into it but how much more clearance should there be compared to the straight up and down measurement? at the moment there is about 1.5thou difference, is that acceptable or should it be less? 3. If i took the engine block + girdle back to the machine shop and got them to line bore the main tunnel (like i told them to do the first time, but they said it didnt need it) what bearing size would i buy? the STD size bearing shells already slide in fairly easily with no real resistance, some even falling out if i tip the girdle up-side-down. If im taking material out of the main tunnel would i need a bearing with extra material on the back side to make up for it? this is probably confusing af to read so if something doesn't make sense let me know and ill try explaining in a different way. My machine shop doesn't come back from christmas break until mid January, hence why i'm asking these questions here. TIA for any help or info 
    • I bought the model back in Japan in Feb. I realised I could never build it, looked around for people who could build it, turns out there's some very skilled people out there that will make copies of 1:1 cars or near enough. I'm not really a photo guy... but people were dragging me in a group chat for the choice of bumper as someone else saw the car before it was finished as they are also a customer of that shop. I took the photo in the above post because I was pretty confident that the lip would work wonders for it. Here's some more in-progress and almost-done pics. It gives a good enough idea as to what the rear looks like!   I have also booked in a track day at the end of January. Lets all hope that is nothing but pure fun and games. If it's not pure fun and games, well, I've already got half an engine spare in the cupboard 
    • Well, do ya, punk? Seriously though, let's fu<king go! The colour and kit looks amazing on the car. Do you have any shots from the rear? I don't quite follow how the model came around. You bought the white kit and he modified it to match your car? Looks nuts either way!
×
×
  • Create New...